The Journal of Research of the National Institute of Standards and Technology is a publication of the U.S. Government. The papers are in the public domain and are not subject to copyright in the United States. However, please pay special attention to the individual works to make sure there are no copyright restrictions indicated. Individual works may require securing other permissions from the original copyright holder.
Volume
113
Journal of Research of the National Institute of Standards and Technology
Abstract
Calcium phosphate cements (CPCs) were prepared using mixtures of tetracalcium phosphate (TTCP) and dicalcium phosphate anhydrous (DCPA), with TTCP/DCPA molar ratios of 1/1, 1/2, or 1/3, with the powder and water as the liquid. Diametral tensile strength (DTS), porosity, and phase composition (powder x-ray diffraction) were determined after the set specimens have been immersed in a physiological-like solution (PLS) for 1 d, 5 d, and 10 d. Cement dissolution rates in an acidified PLS were measured using a dual constant composition method. Setting times ((30 +/- 1) min) were the same for all cements. DTS decreased with decreasing TTCP/DCPA ratio and, in some cases, also decreased with PLS immersion time. Porosity and hydroxyapatite (HA) formation increased with PLS immersion time. Cements with TTCP/DCPA ratios of 1/2 and 1/3, which formed calcium-deficient HA, dissolved more rapidly than the cement with a ratio of 1/1. In conclusion, cements may be prepared with a range of TTCP/DCPA ratios, and those with lower ratio had lower strengths but dissolved more rapidly in acidified PLS.
Addeddate
2011-05-18 20:47:03
Cite
J. Res. Natl. Inst. Stand. Technol. Vol. 113, No. 6, p. 311
Live Music Archive
Librivox Free Audio
Metropolitan Museum
Cleveland Museum of Art
Internet Arcade
Console Living Room
Books to Borrow
Open Library
TV News
Understanding 9/11